Third-order nonlinear optical response and photoluminescence characterization of tellurite glasses with different alkali metal oxides as network modifiers

R. Castro-Beltrán, H. Desirena, G. Ramos-Ortiz, E. De la Rosa, G. Lanty, J. S. Lauret, S. Romero-Servin, and A. Schülzgen, J. Appl. Phys. 110, 083110 (2011)

Studies of the third-order nonlinear optical properties in TeO2-MO-R2O glasses with three different alkali metal oxides R2O (R = Li, Na, K) as network modifiers and two network intermediates MO (M = Zn, Mg) are reported. The influence of such modifiers and intermediates on the nonlinear optical properties of these glasses was investigated using the standard Z-scan and the thermally managed Z-scan techniques under femtosecond pulse excitation at 800 nm. For different modifiers and intermediates, the nonlinear refraction indices n2 of these glasses varied in the range 1.31–2.81 (×10–15 cm2/W). It was found that n2 increases as the ionic radius of both network modifiers and intermediates decreases. Furthermore, the measurements show that the contribution from thermo-optical effects to the nonlinear refraction index is negligible for all of the studied glass compositions. In addition, the effect of modifiers and intermediates in the formation of localized states in the vicinity of the optical bandgap was also studied through photoluminescence experiments. These experiments revealed the presence of two emission bands (red and blue) originating from these localized states that can be populated after optical excitation and subsequent relaxation.

Type :

Publication